WEDOLiT EP 1090-E is a highly viscous, high-performance, mineral-oil-based forming oil. The product has been developed to the highest technical standard for utilization in the pipe industry (e.g. manufacturing of large diameter pipes, for gas and oil pipelines). The product can be used undiluted and prevents the stick-slip- effect due to the high content of polar additives.

• Very high film stability (even under high pressures)
• Good adhesion properties on smooth surfaces, very good wear protection
• Easily removable with water (spontaneous emulsification)
• The emulsion can be used for pre- and post-cleaning of the pipes and the expander head and can be easily separated into water and oily waste by the utilization of specific additives
• The treated water can be reused for the preparation of a new emulsion (to a certain degree)

WEDOLiT EP 435 E is a highly viscous, high-performance forming oil based on renewable raw materials. The product has been developed to the highest technical standard for the utilization in the pipe industry (e.g. manufacturing of large diameter pipes, for gas and oil pipelines). The product can be used undiluted and prevents, due to the high content of polar additives, the stick-slip-effect.

• Very high film stability (even under high pressures)
• Good adhesion properties on smooth surfaces, very good wear protection
• Easily removable with water (spontaneous emulsification)
• The emulsion can be used for pre- and post-cleaning of the pipes and the expander head and can be separated into water and oily waste by the utilization of specific additives
• The treated water can be reused for the preparation of a new emulsion (to a certain degree)

WEDOLiT FN 1190-2300 is a highly viscous, chlorine containing forming oil for tube drawing and other cold forming operations of stainless steel. The undiluted product is usually applied by brushes or by means of rollers.

• Stable load carrying capacity and a homogenous sliding behavior
• Reduces friction and wear and thus contributes to a high tool life
• Outstanding wetting ability and film formation without adhesion
• Stable cold start behavior, prevents stick-slip and chatter
• Leads to clean surfaces and contributes to achieving dimensional accuracy
• Easily removable with organic solvents or alkaline industrial cleaners
• Soluble in chlorinated hydrocarbons

WEDOLiT FN 4455-55 is a low viscous, water-insoluble lubricant for heavy forming operations of steel and non-ferrous metals. A combination of EP additives offers a outstanding performance for precision cutting operations. The undiluted product is usually applied by spraying, dipping, brushing, or rolling.

• Stable load carrying capacity and a homogenous sliding behavior
• Reduces friction and wear and thus contributes to a long tool life
• Outstanding wetting ability and film formation without adhesion
• Stable cold start behavior, prevents stick-slip and chatter
• Leads to clean surfaces and contributes to dimensional accuracy
• Easily removable with organic solvents or alkaline industrial cleaners

WEDOLiT FN 8850-90 is a medium viscous, water-insoluble lubricant for tube drawing and other cold forming operations of steel. Due to the fact that the product also offers corrosion protection, no additional treatment is necessary (for short term storage). The undiluted product is usually applied by spraying, brushes, or by means of rollers.

• Stable load carrying capacity and a homogenous sliding behavior
• Reduces friction and wear and thus contributes to a high tool life
• Outstanding wetting ability and film formation without adhesion
• Stable cold start behavior, prevents stick-slip and chatter
• Leads to clean surfaces and contributes to achieving dimensional accuracy
• Easily removable with organic solvents or alkaline industrial cleaners

WEDOLiT FS 3910 is non-water-soluble cooling lubricant with low viscosity for punching- and bending operations on steel and zinc coated steel. The product is not applicable for the treatment of nonferrous metals.

• Can be applied undiluted by spraying, flooding, brushing or rolling
• Has a good spread effect, which causes an optimal even wettability of metal surfaces
• Has a simultaneously cleaning effect
• Contains a combination of aromatic free solvents with additives of esters and extreme-pressure compounds and is therefore practically odorless
• Is marked by a very fast evaporation with high flash point

WEDOLiT FW 1960 is a water-soluble alkaline soap for heavy drawing operations of steel tubes. The product is usually used as an immersion bath (bath temperature 167 - 194 °F, (75 – 90 °C)).

• The product is designed to react with the zinc phosphate layer (which acts as lubricant) to form a zinc soap. The zinc phosphate layer should be at least 4 μm (at heavy forming operations, e.g. cold extrusion, up to 10 μm). Due to specific additives, a maximum conversion of zinc phosphate and the drawing media occurs, which results in an optimal performance regarding degree and rate of deformation
• Can be used in very low concentrations of 5 - 10% as an aqueous solution (tube drawing). The best results are obtained with water free media
• Offers (in combination with a zinc phosphate layer) very high cross-sectional reduction and high drawing velocities – up to 100 m/min (steel tubes with standard cross-sectional reduction)

WEDOLiT FW 3500 is a high-pressure agent for hydroforming-processes such as internal and external high pressure forming of steel plates, with different surface qualities and thicknesses. The product can also be applied in different grinding and cooling operations.

Approved by “FF Fluid Forming“

• Offers very good high-pressure properties
• Contributes to a high tool life
• Very good application stability
• Almost free of foam
• Offers very good skin compatibility


Recommended mixing ratio
• Hydrofroming:  from 5 - 10%
• Grinding:  from 3 - 6%

WEDOLiT FW 3500 is a high-pressure agent for hydroforming-processes such as internal and external high pressure forming of steel plates, with different surface qualities and thicknesses. The product can also be applied in different grinding and cooling operations.

Approved by “FF Fluid Forming“

• Offers very good high-pressure properties
• Contributes to a high tool life
• Very good application stability
• Almost free of foam
• Offers very good skin compatibility


Recommended mixing ratio
• Hydrofroming:  from 5 - 10%
• Grinding:  from 3 - 6%

WEDOLiT FW 7651 is suitable for the manufacturing of welded steel tubes. It fulfills the requirements regarding lubrication and cleanliness of the tubes and rollers as well as the corrosion protection of the tubes and the system (in a concentration of 4 - 6%).

• Due to its thermal stability, the product can be used in the whole production line (forming, welding, calibration, sawing)
• No emulsification of mineral oils and engine lubricants. Therefore, the application of an anticorrosion oil is possible (e.g. on the Turk’s head of the tube welding engine in the manufacture of profiled tubes)
• Can be centrifuged without loss of active substances
• Removable with organic solvents or alkaline industrial cleaners
• A bright workpiece surface is obtained after annealing


Recommended mixing ratio
• Tube welding:  from 4 - 6%

WEDOLiT FW 7661 is suitable for the manufacturing of welded steel tubes. It fulfils the requirements regarding lubrication and cleanliness of the tubes and rollers as well as the corrosion protection of the tubes and the system (in a concentration of 3 - 5%).

• Due to its thermal stability, the product can be used in the whole production line (forming, welding, calibration, sawing)
• No emulsification of mineral oils and engine lubricants. Therefore, the application of an anticorrosion oil is possible (e.g. on the Turk’s head of the tube welding engine in the manufacturing of profiled tubes)
• Can be centrifuged without loss of active substances
• Removable with organic solvents or alkaline industrial cleaners
• A bright workpiece surface is obtained after annealing


Recommended mixing ratio
• Tube welding:  3 -5%

WEDOLiT FW 7840 is suitable for the manufacturing of welded steel tubes. It fulfils the requirements regarding lubrication and cleanliness of the tubes and rollers as well as the corrosion protection of the tubes and the system (in a concentration from 7%).

The product is approved by Mercedes-Benz Group AG (formerly Daimler AG) (QSO 040305) under the name WEDOLiT K 911.

• Due to its thermal stability, the product can be used in the whole production line (forming, welding, calibration, sawing)
• Can be centrifuged without loss of active substances
• Removable with organic solvents or alkaline industrial cleaners
• A bright workpiece surface is obtained after annealing


Recommended mixing ratio
• Tube welding:  from 7%

WEDLiT N 22-3 is a thixotropic, non water soluble, deep drawing agent, which was developed for cold forming of coated carbon steels. It is especially applicable for electro galvanized zinc-, zinc nickel coated-, and aluminized-sheets. Also good for aluminum and aluminum alloys. The product can be applied by spraying, flooding, or rolling.

Fulfills the requirements of all German automotive manufacturers according to VDA-213 and VW-A001, and has been approved by all VDA members.

• Applications at ambient temperatures possible
• A preheating of the oil to approximately 104 - 122°F, (40 - 50°C) is possible without the loss of the thixotropic effect after cooling
• Acts at the same time as a corrosion protection agent, and therefore a post treatment of the drawn sheets is not necessary
• An agent stable film is formed after drawing
• Can be removed with organic solvents or water soluble, mild alkaline industrial cleaning agents, even after long storage periods
• After grease removal, excellent phosphating is possible

WEDOLiT N 52 is a mineral-oil based high-performance lubricant, suitable for all kinds of minimum quantity lubrication systems such as milling, sawing, or thread forming steel, aluminum, and non-ferrous metals*.
Approved by Rattunde & Co as a cutting oil for minimum quantity lubrication.

• Stable load carrying capacity and a homogenous sliding behavior
• Very good wetting ability and film formation without adhesion
• The outstanding cooling and lubrication properties lead to significantly reduced friction and wear and thus contribute to a long tool life
• Leads to clean surfaces and contributes to achieving dimensional accuracy
• Economical application
• Easily removable with organic solvents or alkaline industrial cleaners